PolyWood™

PolyWood™ is a wood mimic filament without actual wood powder, which removes all risks of nozzle clogs. PolyWood™ is made entirely with PLA using a special foaming technology. It exhibits the same density and appearance as wood.

This Specialty family provides unique filaments from Polymaker to unlock new 3D printing applications.

Available Colors:

Wood

Diameter Size:

1.75 mm, 2.85 mm

Net Weight:

600 g

Buy now

Print Settings

Nozzle Temperature:

190˚C – 210˚C

Printing Speed:

30mm/s – 50mm/s

Bed Temperature

25˚C – 60˚C

Bed Surface:

Glass with glue, blue tape, BuilTak®

Cooling Fan:

ON

Mechanical Properties

Young's Modulus:

2636 ± 330 Mpa

Tensile Strength:

23.2 ± 0.4 Mpa

Elongation at Break:

Shore Hardness:

Bending Strength:

52.9 ± 0.3 Mpa

Charpy Impact:

2.1 ± 0.2 kJ/m2

Thermal Propertises

Glass Transition Temperature:

62˚C

Vicat Softening Temperature:

60˚C

Melting Temperature:

151˚C

Notes

Drying Settings:

55˚C for 6h

Recommended Support Materials

30mm/s – 50mm/s

Other:

25˚C – 60˚C

PolyWood™ features Polymaker's Jam-Free™ technology and Polymaker's Stabilized Foaming™ technology: Jam-Free™ technology improves the heat stability of Polymaker’s PLA filaments with softening temperatures over 140 °C. As a result, Polymaker’s PLA filaments show minimal softening in the “cold end” and can melt rapidly once entering the heating zone, leading to excellent printing quality with zero risk of nozzle jams. Stabilized Foaming™ technology is used to produce foamed filaments, whose foam structure can survive the printing process and be inherited by the printed parts. This enables light weight 3D printed parts with unprecedented surface finish.

Print Settings

Compatible Material:

Maximum Part Size (Diameter*Height):

Polishing Liquid:

Polishing Time:

Operating Temperature

Storage Temperature:

Power Supply (INPUT):

Power Supply (OUTPUT):

Polysher™ INPUT:

Desiccant Type:

Humidity Range:

Resolution

Response

Temperature Range:

Battery specifications

Operation Manual:

Download

PolyWood™ features Polymaker's Jam-Free™ technology and Polymaker's Stabilized Foaming™ technology: Jam-Free™ technology improves the heat stability of Polymaker’s PLA filaments with softening temperatures over 140 °C. As a result, Polymaker’s PLA filaments show minimal softening in the “cold end” and can melt rapidly once entering the heating zone, leading to excellent printing quality with zero risk of nozzle jams. Stabilized Foaming™ technology is used to produce foamed filaments, whose foam structure can survive the printing process and be inherited by the printed parts. This enables light weight 3D printed parts with unprecedented surface finish.